Manufacturing Resistance Wires 99.6% Ni200 Pure Nickel Wire With Higher Thermal Conductivity
Product Introduction
Ni200 pure nickel wire is a filamentous material made of high-purity (99.6%) nickel, with excellent mechanical properties and corrosion resistance, high thermal and electrical conductivity, low gas content, and low vapor pressure. In its chemical composition, the content of nickel (with cobalt added) is as high as 99.0%, while the content of other elements such as copper, iron, manganese, carbon, silicon, and sulfur is controlled within an extremely low range. The physical properties of Ni200 pure nickel wire include a density of 8.89 g/cm ³, a melting point of 1435-1446 ° C, an expansion coefficient of 13.2 μ m/m · ℃ at 100 ° C, a thermal conductivity of 73.4 W/m · ℃ at 100 ° C, and a resistance coefficient of 0.125 μ Ω· m at 100 ° C.
Parameter
| Grade | Ni+Co | Cu | Si | Mn | C | Mg | S | P | Fe |
| N4 | 99.8 | 0.015 | 0.03 | 0.002 | 0.01 | 0.01 | 0.001 | 0.001 | 0.04 |
| N6 | 99.6 | 0.10 | 0.10 | 0.05 | 0.10 | 0.10 | 0.005 | 0.002 | 0.10 |
| Ni201 | ≥99.0 | ≤0.25 | ≤0.35 | ≤0.35 | ≤0.02 | / | ≤0.01 | / | ≤0.40 |
| Ni200 | ≥99.2 | ≤0.25 | ≤0.35 | ≤0.35 | ≤0.15 | / | ≤0.01 | / | ≤0.40 |
| Product Attribute | Description |
| Standard | ASTM B164 |
| Trade Name | UNS N02200/Nickel 200/2.4060/NS5200/N5 |
| Tensile Strength | 600-800 MPa |
| Color | Silvery White |
| Shape | Wire |
| Magnetic Properties | Non-magnetic |
| Size | 0.025-10mm, Can Customized |
| Melting Point | 1455°C |
| Density | 8.9 G/cm³ |
| Packing | Spool, Coil, Or As Per Customer's Request |
Specific Applications
Ni200 pure nickel wire is widely used in multiple fields:
- In the field of electronics: used for manufacturing resistance wires, resistors, temperature sensors, and electronic chips. Its stable resistance value and temperature coefficient can provide accurate measurement results over a wide temperature range, making it widely used in high-temperature environments in industries such as petroleum, chemical, and power.
- In the field of chemical engineering: used for manufacturing corrosion-resistant equipment and liners for chemical reactors, especially suitable for corrosion resistance to caustic soda. Under high temperature conditions above 300 ℃, it can be used as equipment for manufacturing industrial sodium hydroxide.
- Aerospace field: High temperature components used for manufacturing aircraft engines and structural materials for spacecraft. Ni200 pure nickel wire has excellent high-temperature performance and radiation resistance, which can withstand extreme environmental conditions and ensure the reliability and safety of equipment.
- Food processing and salt extraction: Ni200 pure nickel wire is also widely used in food processing equipment and salt extraction equipment due to its good corrosion resistance and mechanical properties, which can ensure stable operation of equipment in harsh environments.
Advantages and Characteristics
- Excellent corrosion resistance: Ni200 pure nickel wire exhibits excellent corrosion resistance to many acidic and alkaline media, especially in reducing acid and hydrofluoric acid environments. It has good corrosion resistance to many acid, alkali, salt solutions, and organic solvents at room temperature.
- Good electrical heating performance: low resistivity, high thermal conductivity, capable of effectively conducting current and heat, suitable for precision component manufacturing in the electronic and electrical fields.
- High mechanical strength: It has good mechanical strength and toughness, can maintain stable performance in high temperature and high pressure environments, and is suitable for key components in aerospace and chemical industries.
- Weldability and processability: With excellent weldability and processability, it can be processed into various forms of products such as pipes, rods, wires, plates, strips, foils, etc.
Contact Us
Email:fbwlau@cnrunlai.com
Oem service:
Welcome customized size
We are experience factory for OEM&ODM service
Q&A
Q1: What is the difference between Ni200 pure nickel wire and Ni201 pure nickel wire?
A1: Ni200 and Ni201 are both high-purity nickel materials, but Ni201 has a lower carbon content (up to 0.02%), making it more suitable for use in high-temperature environments above 315 ° C. Ni200 has a maximum carbon content of 0.15% and is suitable for environments below 315 ° C.
Q2: What are the problems with Ni200 pure nickel wire at high temperatures?
A2: Ni200 pure nickel wire may undergo graphitization at temperatures above 315 ° C, resulting in severe performance damage. Therefore, for applications that require use at temperatures above 315 ° C, Ni201 is more recommended.
Q3: What is the processing performance of Ni200 pure nickel wire?
A3: Ni200 pure nickel alloy has excellent ductility and toughness, making it easy to process and shape. It can change the grain structure and shape of alloys through cold and hot processing, increase strength and hardness, and improve the mechanical properties of materials.